Item Description
Textile ceramics are primarily developed from alumina ceramic materials, which have outstanding complete technical properties such as higher mechanical toughness, higher hardness, low large-frequency dielectric loss, high temperature insulation resistance, chemical resistance and good thermal conductivity.
Content alternative:
Steatite
Alumina up to ninety nine.7 % or 95% alumina
Titania
Zirconia
Assortment of items:
Flange Eyelet, Double flange eyelet, Slotted eyelet, groove eyelets, phase eyelet, Minimize Eyelet, Action Eyelets, Tubes, Rods, Sleeve,
Ring, Bush, Disc, Dish, Washer, Plates Entice Xihu (West CZPT ) Dis., Traverse Xihu (West CZPT ) Dis., Pig tail Xihu (West CZPT ) Dis., Pet tail Xihu (West CZPT ) Dis., Rollers, Oilers, Oiling Nozzles Cutters
Software :
Yarn producing devices
Twister equipment
Airjet looms
Circular looms
weaving devices
winder equipment
Rope,Tap vegetation
Tailored guides as per comprehensive drawings and technical specs.
Substance info:
|
Product |
Unit |
ninety five% al2o3 |
ninety nine% al2o3 |
Zirconia |
Black Tio2 |
Yellow Tio2 |
|
Coloration |
|
white,pink |
product,pink |
white,black,yellow |
Black |
Yellow |
|
Density |
g/cm3 |
three.65 |
three.nine |
6 |
four |
4 |
|
Flexural power |
MPA |
290 |
390 |
1300 |
70 |
70 |
|
Compressive strength |
MPA |
3300 |
3900 |
3000 |
600 |
600 |
|
Vickers hardness |
HV0.five |
1800 |
2000 |
1150 |
900 |
900 |
|
Thermal expansion cofficient |
ten-6 K-3 |
5-8.three |
five.4-8.three |
ten |
eight.5 |
8.5 |
|
Thermal conductivity |
w/mk |
23 |
28 |
two |
twenty five |
25 |